Ohmalloy Material Co.,Ltd
| Payment Terms | L/C, T/T |
| Delivery Time | 15 workdays |
| Packaging Details | coil |
| Material | FeNi |
| Shape | strip |
| Application | precision instrument industry |
| Chemical composition | Ni Fe Co V |
| Product name | 4J29 |
| Density | 8.20g/cm3 |
| Standard | GB ASTM AISI,ASTM/ASME/AISI/GB/DIN |
| Color | Silvery White,bright |
| Surface | Bright |
| Feature | low coeffficient of expansion from Cryogenic temperature |
| Brand Name | Ohmalloy |
| Model Number | 4J29 |
| Certification | ISO CE |
| Place of Origin | China |
View Detail Information
Explore similar products
2.0mm Bright Surface Precision Alloys , Low Expansion Alloys For Sealing Glass
Bright Surface Fe Ni Precision Alloys With Wooden Case / Spool Package
Vacuum Furnace Nickel Based Alloys For Glass - To - Metal Seal Vacuum Switch
0.2×30 mm Precision Alloys Invar Alloy Strip 8.2 g/cm3 Density 6.0mm ~ 250mm
Product Specification
| Payment Terms | L/C, T/T | Delivery Time | 15 workdays |
| Packaging Details | coil | Material | FeNi |
| Shape | strip | Application | precision instrument industry |
| Chemical composition | Ni Fe Co V | Product name | 4J29 |
| Density | 8.20g/cm3 | Standard | GB ASTM AISI,ASTM/ASME/AISI/GB/DIN |
| Color | Silvery White,bright | Surface | Bright |
| Feature | low coeffficient of expansion from Cryogenic temperature | Brand Name | Ohmalloy |
| Model Number | 4J29 | Certification | ISO CE |
| Place of Origin | China | ||
| High Light | 4J29 Expansion Precision Alloys ，Permalloy Iron Nickel Alloy ，ASTM Expansion Precision Alloys | ||
4J29 strip 0.2mm*95mm Precision expansion alloy Iron-Nickel Alloy permalloy coil / foil
OHMALLOY
OhmAlloy-4J29 (Expansion alloy)
(Common Name: Kovar, Nilo K, KV-1, Dilver Po, Vacon 12)OhmAlloy-4J29 also known as Kovar alloy. it was invented to meet the need for a reliable glass-to-metal seal, which is required in electronic devices such as light bulbs, vacuum tubes, cathode ray tubes, and in vacuum systems in chemistry and other scientific research. Most metals cannot seal to glass because their coefficient of thermal expansion is not the same as glass, so as the joint cools after fabrication the stresses due to the differential expansion rates of the glass and metal cause the joint to crack.
OhmAlloy-4J29was invented to meet the need for a reliable glass-to-metal seal, which is required in electronic devices such as light bulbs, vacuum tubes, cathode ray tubes, and in vacuum systems in chemistry and other scientific research. Most metals cannot seal to glass because their coefficient of thermal expansion is not the same as glass, so as the joint cools after fabrication the stresses due to the differential expansion rates of the glass and metal cause the joint to crack.
OhmAlloy-4J29 not only has thermal expansion similar to glass, but its nonlinear thermal expansion curve can often be made to match a glass, thus allowing the joint to tolerate a wide temperature range. Chemically, it bonds to glass via the intermediate oxide layer of nickel oxide and cobalt oxide; the proportion of iron oxide is low due to its reduction with cobalt. The bond strength is highly dependent on the oxide layer thickness and character. The presence of cobalt makes the oxide layer easier to melt and dissolve in the molten glass. A grey, grey-blue or grey-brown color indicates a good seal. A metallic color indicates lack of oxide, while black color indicates overly oxidized metal, in both cases leading to a weak joint.
Mainly used in electric vacuum components and emission control, shock tube, igniting tube, glass magnetron, transistors, seal plug, relay, integrated circuits lead, chassis, brackets and other housing sealing.
Normal composition%
| Ni | 28.5~29.5 | Fe | Bal. | Co | 16.8~17.8 | Si | ≤0.3 |
| Mo | ≤0.2 | Cu | ≤0.2 | Cr | ≤0.2 | Mn | ≤0.5 |
| C | ≤0.03 | P | ≤0.02 | S | ≤0.02 |
Tensile Strength, MPa
| Code of condition | Condition | Wire | Strip |
| R | Soft | ≤585 | ≤570 |
| 1/4I | 1/4 Hard | 585~725 | 520~630 |
| 1/2I | 1/2 Hard | 655~795 | 590~700 |
| 3/4I | 3/4 Hard | 725~860 | 600~770 |
| I | Hard | ≥850 | ≥700 |
Typical Physical properties
| Density (g/cm3) | 8.2 |
| Electrical resistivity at 20ºC(Om*mm2/m) | 0.48 |
| Temperature factor of resistivity(20ºC~100ºC)X10-5/ºC | 3.7~3.9 |
| Curie point Tc/ ºC | 430 |
| Elastic Modulus, E/ Gpa | 138 |
Coefficient of expansion
| θ/ºC | α1/10-6ºC-1 | θ/ºC | α1/10-6ºC-1 |
| 20~60 | 7.8 | 20~500 | 6.2 |
| 20~100 | 6.4 | 20~550 | 7.1 |
| 20~200 | 5.9 | 20~600 | 7.8 |
| 20~300 | 5.3 | 20~700 | 9.2 |
| 20~400 | 5.1 | 20~800 | 10.2 |
| 20~450 | 5.3 | 20~900 | 11.4 |
Thermal conductivity
| θ/ºC | 100 | 200 | 300 | 400 | 500 |
| λ/ W/(m*ºC) | 20.6 | 21.5 | 22.7 | 23.7 | 25.4 |
| The heat treatment process | |
| Annealing for stress relief | Heated to 470~540ºC and hold 1~2 h. Cold down |
| annealing | In vacuum heated to 750~900ºC |
| Holding time | 14 min~1h. |
| Cooling rate | No more than 10 ºC/min cooled to 200 ºC |
Style of supply
| Alloys Name | Type | Dimension | ||
| OhmAlloy-4J29 | Wire | D= 0.1~8mm | ||
| OhmAlloy-4J29 | Strip | W= 5~250mm | T= 0.1mm | |
| OhmAlloy-4J29 | Foil | W= 10~100mm | T= 0.01~0.1 | |
| OhmAlloy-4J29 | Bar | Dia= 8~100mm | L= 50~1000 | |
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Exporter,Trading Company
Year Established:
2008
Total Annual:
4000000-6000000
Employee Number:
20~50
Ecer Certification：
Verified Supplier
Ohmalloy Material Co.,Ltd is a high-tech enterprise which specialized in making all kinds of alloy such as high resistance alloy, low-resistance copper nickel alloy, precision alloy, FeCrAl alloy and thermocouple Alloy. Ohmalloy Material Co.,Ltd have a full production line from melting, surface... Ohmalloy Material Co.,Ltd is a high-tech enterprise which specialized in making all kinds of alloy such as high resistance alloy, low-resistance copper nickel alloy, precision alloy, FeCrAl alloy and thermocouple Alloy. Ohmalloy Material Co.,Ltd have a full production line from melting, surface...