| Productn Name | PEEK |
| Color | Natural/White/Yellow/Red |
| Density(g/cm3) | 1.32/1.48/1.51/1.35 |
| Bending Strength(MPa) | 163/152/154/158 |
| Bending ModulusBending ModulusBending Modulus(GPa) | 4/5.3/5.6/4.8 |
| Bending Modulus(KJ/m2) | 199/145/162/176 |
| Brand Name | Leomed |
View Detail Information
Explore similar products
Yellow Dental Ceramic Glaze Porcelain Powder CE For Ceramic Glazing
Glazing Powder Dental Zirconia Coloring Liquid Ceramics Class II Instrument
Precision PMMA Discs for CAD/CAM BL1-BL4 & Clear Options Night Guards / Bridges
Millable Dental PMMA Discs CAD/CAM Ready Flexible / Multilayer Types Vita 16
Product Specification
| Productn Name | PEEK | Color | Natural/White/Yellow/Red |
| Density(g/cm3) | 1.32/1.48/1.51/1.35 | Bending Strength(MPa) | 163/152/154/158 |
| Bending ModulusBending ModulusBending Modulus(GPa) | 4/5.3/5.6/4.8 | Bending Modulus(KJ/m2) | 199/145/162/176 |
| Brand Name | Leomed | ||
| High Light | Amann Girrbach PEEK Dental Discs ，Zirkonzahn Precision PEEK Dental Discs ，160MPa+ Precision PEEK Dental Discs | ||
Designed for permanent implant prosthetics, these medical-grade PEEK discs deliver bone-like elasticity (4-5.6GPa modulus) and >160MPa bending strength – enabling metal-free solutions for high-stress dental applications. The semi-crystalline thermoplastic retains dimensional integrity at 260°C, ensuring sub-50μm accuracy in CAD/CAM workflows.
Cortical Bone-Matched Stiffness: 4.0-5.6GPa modulus eliminates stress shielding
Fatigue Resistance: 160MPa+ flexural strength supports multi-unit bridges
Bioinert Surface: ISO 10993-certified, inhibits bacterial colonization
Radiolucency: Zero imaging artifacts in CT/MRI scans
| Property | PEEK Discs | Titanium Abutments | PMMA Temporaries |
| Elastic Modulus (GPa) | 4.0-5.6 | 110-120 | 2.0-3.0 |
| Density (g/cm³) | 1.32-1.51 | 4.4-4.5 | 1.15-1.19 |
| Allergy Risk | None | >8% Nickel Sensitivity | <0.1% |
| Aesthetic Adaptability | ★★★★☆ (Tintable) | ★☆☆☆☆ | ★★★★★ |
Tool Selection
Diamond-coated carbide burs
Spindle speed: 18,000-25,000 RPM
Workholding
Vacuum pressure ≥0.75 MPa
3mm edge margin required
Post-Processing
Sandblasting: 50μm alumina oxide
Staining: PEEK-specific dyes (80°C/10min)
► Healing Abutments
- Osteoblast proliferation rate ↑37% vs. titanium
► Removable Partial Dentures
- 60% lighter than cobalt-chrome frameworks
► Surgical Guides
- Withstands 200+ autoclave cycles (134°C)
| Property | Natural | White | Yellow | Red |
| Density (g/cm³) | 1.32 | 1.48 | 1.51 | 1.35 |
| Flexural Strength (MPa) | 163 | 152 | 154 | 158 |
| Modulus (GPa) | 4 | 5.3 | 5.6 | 4.8 |
| Fracture Toughness (KJ/m²) | 199 | 145 | 162 | 176 |
Company Details
Business Type:
Manufacturer,Trading Company
Year Established:
2019
Total Annual:
1000000-1500000
Employee Number:
100~150
Ecer Certification：
Verified Supplier
Chongqing Leomed Technology Co., Ltd. is a rapidly growing and professional company that specializes in providing dental CAD/CAM solutions to customers worldwide. With a strong focus on “innovation, precision, validation, and customer satisfaction”, we invest significant efforts in resea... Chongqing Leomed Technology Co., Ltd. is a rapidly growing and professional company that specializes in providing dental CAD/CAM solutions to customers worldwide. With a strong focus on “innovation, precision, validation, and customer satisfaction”, we invest significant efforts in resea...