| Diameter Range | 4 mm to 350 mm |
| Length | 1m / 2m / 3m / 6m or custom |
| Surface Finish | Bright, Polished, Mill Finish |
| Density Monel 400 | 8.8 g/cm³ |
| Density Monel K500 | 8.6 g/cm³ |
| Melting Point Monel 400 | 1300°C - 1350°C |
| Melting Point Monel K500 | 1260°C - 1300°C |
| Tensile Strength Monel 400 | 690 - 1000 MPa |
| Tensile Strength Monel K500 | 1100 - 1300 MPa |
| Yield Strength Monel 400 | 240 MPa |
| Yield Strength Monel K500 | 550 MPa |
| Elongation Monel 400 | ≥ 40% |
| Elongation Monel K500 | ≥ 25% |
| Hardness Monel 400 | 150 - 200 HB |
| Hardness Monel K500 | 350 - 400 HB |
| Certification | ISO, AISI, ASTM, GB, EN, DIN |
View Detail Information
Explore similar products
PPGI Steel Coil with Z60-Z275 Zinc Coating for Container Plate Application in
Hastelloy C-22 Round Bar ASTM B574 with Superior Pitting/Crevice Corrosion
Customized JIS CGCC Soft Prepainted Galvanized Steel Sheet with 1220*2440mm
Corrosion Resistant Prepainted Color Steel with Custom Sizes and High Durability
Product Specification
| Diameter Range | 4 mm to 350 mm | Length | 1m / 2m / 3m / 6m or custom |
| Surface Finish | Bright, Polished, Mill Finish | Density Monel 400 | 8.8 g/cm³ |
| Density Monel K500 | 8.6 g/cm³ | Melting Point Monel 400 | 1300°C - 1350°C |
| Melting Point Monel K500 | 1260°C - 1300°C | Tensile Strength Monel 400 | 690 - 1000 MPa |
| Tensile Strength Monel K500 | 1100 - 1300 MPa | Yield Strength Monel 400 | 240 MPa |
| Yield Strength Monel K500 | 550 MPa | Elongation Monel 400 | ≥ 40% |
| Elongation Monel K500 | ≥ 25% | Hardness Monel 400 | 150 - 200 HB |
| Hardness Monel K500 | 350 - 400 HB | Certification | ISO, AISI, ASTM, GB, EN, DIN |
| High Light | Corrosion Resistant Monel Round Bar ，Diameter 4-350mm Nickel Alloy Bar ，Hot Rolled Monel Alloy Bar | ||
Monel 400 and Monel K500 are high-performance nickel alloys renowned for exceptional corrosion resistance, mechanical properties, and versatility across numerous industrial applications. Available as round bars in diameters from 4mm to 350mm, these alloys come in both bright bar and hot-rolled bar forms.
| Property | Monel 400 | Monel K500 |
|---|---|---|
| Alloy Type | Nickel-Copper Alloy | Nickel-Copper Alloy with Aluminum & Titanium |
| Diameter Range | 4mm to 350mm | 4mm to 350mm |
| Form | Round Bar, Bright Bar, Hot Rolled Bars | Round Bar, Bright Bar, Hot Rolled Bars |
| Length | Customizable (3m to 6m) | Customizable (3m to 6m) |
| Surface Finish | Bright, Polished, Mill Finish | Bright, Polished, Mill Finish |
| Standards | ASTM B164, ASME SB164, UNS N04400 | ASTM B164, ASME SB164, UNS N05500 |
| Density | 8.8 g/cm³ | 8.6 g/cm³ |
| Melting Point | 1300°C - 1350°C | 1260°C - 1300°C |
| Element | % by Weight |
|---|---|
| Nickel (Ni) | 63.0 - 70.0 |
| Copper (Cu) | 28.0 - 34.0 |
| Iron (Fe) | ≤ 2.5 |
| Manganese (Mn) | ≤ 2.0 |
| Carbon (C) | ≤ 0.3 |
| Silicon (Si) | ≤ 0.5 |
| Sulfur (S) | ≤ 0.024 |
| Element | % by Weight |
|---|---|
| Nickel (Ni) | 63.0 - 70.0 |
| Copper (Cu) | 27.0 - 33.0 |
| Aluminum (Al) | 2.3 - 3.15 |
| Titanium (Ti) | 0.35 - 0.85 |
| Iron (Fe) | ≤ 2.5 |
| Manganese (Mn) | ≤ 1.0 |
| Carbon (C) | ≤ 0.3 |
| Silicon (Si) | ≤ 0.5 |
| Sulfur (S) | ≤ 0.024 |
| Property | Value |
|---|---|
| Tensile Strength | 690 - 1000 MPa |
| Yield Strength | 240 MPa |
| Elongation | ≥ 40% |
| Hardness | 150 - 200 HB |
| Modulus of Elasticity | 210 GPa |
| Poisson's Ratio | 0.31 |
| Fatigue Strength | 220 MPa |
| Property | Value |
|---|---|
| Tensile Strength | 1100 - 1300 MPa |
| Yield Strength | 550 MPa |
| Elongation | ≥ 25% |
| Hardness | 350 - 400 HB |
| Modulus of Elasticity | 220 GPa |
| Poisson's Ratio | 0.31 |
| Fatigue Strength | 350 MPa |
Monel round bars are carefully packaged to prevent damage during transportation. Packaging options include wooden crates for bulk orders, plastic wrapping for smaller quantities, and custom packaging arrangements. Shipping is available by sea, air, or land with typical delivery times of 2-6 weeks for international shipments.
Monel 400 is a pure nickel-copper alloy, while Monel K500 contains additional aluminum and titanium, providing improved strength, hardness, and wear resistance.
Yes, both alloys are weldable, but correct filler materials must be used to maintain their properties.
Monel 400 can be used at temperatures up to 1020°C, while Monel K500 can handle temperatures up to 480°C.
No, both alloys are non-magnetic, making them ideal for applications in sensitive environments.
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Exporter
Total Annual:
>1000000
Employee Number:
>100
Ecer Certification：
Verified Supplier
Our company is located in Wuxi City, China, we are a stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe and other products distribution wholesale private enterprise. Our company operates stainless steel plate, seamless steel pipe, round steel, steel belt, decorative... Our company is located in Wuxi City, China, we are a stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe and other products distribution wholesale private enterprise. Our company operates stainless steel plate, seamless steel pipe, round steel, steel belt, decorative...
Get in touch with us
Leave a Message, we will call you back quickly!